衡陽機械結(jié)構(gòu)用不銹鋼焊接鋼管牌號及熱處理制度參照表大全

衡陽機械結(jié)構(gòu)用不銹鋼焊接鋼管牌號及熱處理制度參照表大全

名  稱	說  明
鋼管外徑和壁厚尺寸規(guī)格	外徑和壁厚按表6-110的規(guī)定(壁厚0.3mm、0.4mm不適用GBT12770---1991)
鋼管尺寸允許偏差	外徑和壁厚允許偏差按表6-111的規(guī)定

牌  號	化學(xué)成分(質(zhì)量分數(shù))(％)
	C	Si	Mn	P	S	Ni	Cr	其  他
00cr19Ni11	≤0.030	≤1.00	≤2.00	≤0.035	≤0.030	9.00-13.00	18.00-20.00
00Cr17Ni14Mo2	≤0.030	≤1.00	≤2.00	≤0.035	≤0.030	12.00-15.00	16.00-18.00	Mo2.00-3.00
0Cr19Ni9	≤0.08	≤1.00	≤2.00	≤0.035	≤0.030	8.00-10.00	18.00-20.00
1Cr18Ni9	≤0.15	≤1.00	≤2.00	≤0.035	≤0.030	8.00-10.00	17.00-19.00
(1Cr18Ni9Ti)	≤0.12	≤1.00	≤2.00	≤0.035	≤0.030	8.00-11.00	17.00-19.00	Ti5(C％-0.02)-0.80
0Cr17Ni12Mo2	≤0.08	≤1.00	≤2.00	≤0.035	≤0.030	10.00-14.00	16.00-18.00	Mo2.00-3.00
0Cr18Ni11NB	≤0.08	≤1.00	≤2.00	≤0.035	≤0.030	9.00-13.00	17.00-19.00	Nb≥10×C％
0Cr25Ni20	≤0.08	≤1.50	≤2.00	≤0.035	≤0.030	19.00-22.00	24.00-26.00
1Cr17	≤0.12	≤0.75	≤1.00	≤0.035	≤0.030		16.00-19.00	Ti或Nb0.10-1.00
1Cr15	≤0.12	≤1.00	≤1.00	≤0.035	≤0.030		16.00-18.00
0Cr13	≤0.08	≤1.00	≤1.00	≤0.035	≤0.030		11.50-13.50
1Cr13	≤0.15	≤1.00	≤1.00	≤0.035	≤0.030		11.50-13.50

序  號	牌  號	推薦熱處理制度
1	00Cr19Ni11	固溶處理	1010-1150℃快冷
2	00Cr17Ni14Mo2		1010-1150℃快冷
3	0Cr19Ni9		1010-1150℃快冷
4	1Cr18Ni9		1010-1150℃快冷
5	(1Cr18Ni9Ti)		1000-1080℃快冷
6	0Cr17Ni12Mo2		1010-1150℃快冷
7	0Cr18Ni11Nb		980-1150℃快冷
8	0Cr25Ni20		1030-1180℃快冷
9	1Cr17	退火處理	780-850℃快冷或緩冷
10	1Cr15		780-850℃快冷或緩冷
11	0Cr13		約750℃快冷或800-900℃緩冷
12	1Crr13		約750℃快冷或800-900℃緩冷

牌  號		力學(xué)性能
		焊后經(jīng)熱處理			焊接態(tài)
		抗拉強度 ób/MPa≥	屈服強度 ó0.2／MPa≥	伸長率 δ5(％)≥	抗拉強度 ób/MPa≥	屈服強度 ó0.2／MPa≥	伸長率 δ5(％)≥
奧氏 體型	00Cr19Ni11	480	180	35	480	180	25
	00Cr17Ni14Mo2
	0Cr19Ni9	520	210		520	210
	1Cr18Ni9
	(1Cr18Ni9Ti)
	0Cr17Ni12Mo2
	0Cr18Ni11Nb
	0Cr25Ni20
鐵素 體型	1Cr17	410	210	20	按雙方協(xié)議
	1Cr15
馬氏 體型	0Cr13	410	210	20
	1Cr13